Basit öğe kaydını göster

dc.contributor.authorYalçıner, Gülüzar
dc.contributor.authorÖzer, Gökhan
dc.contributor.authorKısasöz, Alptekin
dc.contributor.authorKaraaslan, Ahmet
dc.date.accessioned2021-04-22T11:13:47Z
dc.date.available2021-04-22T11:13:47Z
dc.date.issued2019en_US
dc.identifier.citationYALÇINER, Gülüzar, Gökhan ÖZER, Alptekin KISASÖZ & Ahmet KARAASLAN. "Influence of The Phase Balance and Cooling Conditions on The Microstructure and Corrosion Behavior of Solution-treated 1.4462 Duplex Stainless Steel", Materials Research Express, 6.12 (2019): 1-9.en_US
dc.identifier.urihttps://iopscience.iop.org/article/10.1088/2053-1591/ab6f3a
dc.identifier.urihttps://hdl.handle.net/11352/3332
dc.description.abstractIn this study, effect of cooling rate on the microstructure and corrosion behavior of the solutiontreated 1.4462 alloy was investigated. 1.4462 alloy was heat-treated at 1000 °C, 1120 °Cand 1200 °C for different duration in order to obtain various phase balance. Two different cooling regimes (rapid cooling and steady cooling) were applied following the solution treatment processes. Also, effect of sigma phase was investigated together with ferrite and austenite phases for steady cooled samples. After heat treatment processes, samples were characterized by an optical microscope (OM), image analysis and scanning electron microscope (SEM). Moreover, hardness tests and electrochemical corrosion tests were applied. According to results, Ferrite ratio and ferrite grain size were increasing with increasing solution treatment temperature and time. Also, ferrite phase was more dominant compared to sigma phase for hardness of the solution-treated samples. Moreover, existing of sigma in higher amount promoted the observation of Epit value.en_US
dc.language.isoengen_US
dc.publisherIOP Publishingen_US
dc.relation.isversionof10.1088/2053-1591/ab6f3aen_US
dc.rightsinfo:eu-repo/semantics/embargoedAccessen_US
dc.subjectDuplex Stainless Steelen_US
dc.subject1.4462 Alloyen_US
dc.subjectSolution Treatmenten_US
dc.subjectCorrosion Resistanceen_US
dc.titleInfluence of The Phase Balance and Cooling Conditions on The Microstructure and Corrosion Behavior of Solution-treated 1.4462 Duplex Stainless Steelen_US
dc.typearticleen_US
dc.relation.journalMaterials Research Expressen_US
dc.contributor.departmentFSM Vakıf Üniversitesi, Rektörlük, Alüminyum Test Eğitim ve Araştırma Merkezi (ALUTEAM)en_US
dc.contributor.authorIDhttps://orcid.org/0000-0001-5233-8896en_US
dc.identifier.volume6en_US
dc.identifier.issue12en_US
dc.identifier.startpage1en_US
dc.identifier.endpage9en_US
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanıen_US
dc.contributor.institutionauthorÖzer, Gökhan


Bu öğenin dosyaları:

Thumbnail

Bu öğe aşağıdaki koleksiyon(lar)da görünmektedir.

Basit öğe kaydını göster