Purpose – The purpose of this paper is to evaluate the effect of post process combinations, e.g. hot isostatic pressing (HIP) only, HIP 1 T6 heat treatments, and T6 only, with different aging time, on surface properties, ...

In this study, a retrogression process (R) has been applied to AA7075 at 180, 240, and 370°C for 15, 30, 90, and 120 min. After the retrogression, reaging treatment (RA) was reapplied with T6 conditions (120°C for 24 ...

In this study, T651-applied AA7075 alloy was subjected to retrogression and reaging (RRA) process. Various retrogression temperatures (180 °C, 280 °C, 370 ° C) and times (15 min, 30 min, 90 min) were used to determine the ...

The effects of different retrogression times and temperatures on the microstructure, electrical conductivity, exfoliation corrosion (EXCO), and hardness of the 7050 aluminium alloy were compared with the T6 and ...

In this study, AlSi10Mg samples produced by the direct metal laser sintering (DMLS) method were applied to heat treatment with different parameters (stress relief and T6). Heat‐treated and as‐built samples were subjected ...

In this study, 316L stainless steel (SS) samples produced with standard parameters using the Additive Manufacturing method were heat treated with different parameters, and the effects of heat treatment on the microstructure, ...